Modelo: HTPL 80
Marca: Para siempre
Place Of Origin: China
Plastic Molding Process Type: Extruding
Processing Service: Moulding
Operate Temperature: HTPL 65 Operate temperature HTPL 65
Applications: onshore,offshore pipelines
Uso: coating corrosion protection
HSS Width: 300mm,350mm,450mm,500mm
Espesor: 2.0mm,2.2mm,2.5mm
Type: Wrap type with closure patch
Layer: 3PE
Color: Black
Backing Materials: Cross linked PE backing
Adhesive: Hot melt adhesive
| Unidades de venta | : | Roll |
| Tipo de paquete | : | Cartón+paleta |
| Ejemplo de una imagen | : |
|
| Descargar | : |
|
The file is encrypted. Please fill in the following information to continue accessing it
3LPE 80C Las mangas de retiro de calor se desarrollan por siempre sobre la base del producto original. Es el primero del mismo tipo en China. Actualmente, el producto está muy por encima de los estándares profesionales anticorrosivos domésticos y alcanza el requisito estándar de EN12068 , ISO21809-3 y ASTM también.
HT80 es una manga envolvente con un parche de cierre separado, el respaldo reticulado proporciona una abrasión superior, mecánica y química
Resistencia al ataque. El adhesivo de alta temperatura proporciona una excelente resistencia al desestmisión catódica para garantizar la corrosión a largo plazo
Protección, longitudes personalizadas justo en el tiempo permiten que los rollos a granel sean cortados en el campo protegen cualquier tamaño de tubería, La configuración de manga abierta permite el
El producto que se aplicará después de la tubería ha sido soldado y limpiado.
HT80 es un rendimiento superior, un rendimiento se encogen calor de rendimiento diseñados para la protección contra la corrosión en el campo juntas soldadas de circunferencia de canal de las tuberías de acero enterradas y expuestas que funcionan hasta 80 ° C Mangas encogibles de calor cubiertas de 3 lentes de manga de algancio de 3lpe , cinta de encogimiento de calor de 2PE , envoltura de 3lpp alrededor de manga alrededor de
Mangas de envoltura retráctil con calor HDD, parche de cierre de cinta con reducción
 |
| Layer 1:The inner layer is two-components epoxy primer which coated on steel pipe; |
| Layer 2:Intermediate level is special hot melt adhesive ; |
|
Layer 3:Outer layer is modified radiation crossing linking polyethylene backing. |
|
No. |
Property |
Unit |
Test Result |
Test Method |
|
|
PE Backing Layer |
|||||
|
1 |
PE Backing Layer Thickness, at 23 ℃ |
mm |
0.8/1.2/1.5 |
ASTM D 1000- 17 |
|
|
2 |
Tensile Strength (50mm/min), at 23 ℃ |
PSI |
3200 |
ASTM D638-22 |
|
|
3 |
Elongation at Break (50mm/min), at 23 ℃ |
% |
550 |
ASTM D638-22 |
|
|
4 |
Dielectric Strength, at 23 ℃ |
KV/mm |
35 |
ASTM D 149-20 |
|
|
6 |
Linear Thermal Shrinkage |
% |
35 |
ASTM D2732- 14 |
|
|
Adhesive Layer |
|||||
|
1 |
Adhesive Layer Thickness, at 23 ℃ |
mm |
1.00/1.30 |
ASTM D 1000- 17 |
|
|
2 |
Ring and Ball Softening Point |
℃ |
120 |
ASTM E28- 18 |
|
|
3 |
Adhesive Lap Joint Shear Strength |
PSI |
600 |
ASTM D 1002- 10 |
|
|
Heat Shrinkable Sleeves Coatings Physical Properties |
|||||
|
1 |
Impact Resistance, at 23℃ |
|
≥15 |
19.6 |
EN 12068:1999 |
|
2 |
Shore Hardness, at 23℃ |
D |
≥50 |
55 |
ASTM D2240- 15 |
|
3 |
Peel strength (10mm/min), to PE ° |
N/cm |
≥10.0 |
110 |
DIN 30672-2000 |
|
4 |
Cathodic Disbondment 30d, at 60℃ |
mm |
≤25 |
12 |
ASTM G42- 11 |
Sobre Nosotros
Contal Us
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now